Iron oxide-based magnetic nanoparticles (MNPs) play a major role as contrast agents for magnetic resonance imaging (MRI). The introduction of ${\text{Zn}}^{2+}$ and ${\text{Mn}}^{2+}$ ions within their crystal lattice alters the magnetic anisotropy and the spin dynamical properties of the systems, which in turn influence the nuclear relaxation mechanisms that drive contrast enhancement in MRI. This work explored two sets of doped-magnetite MNPs (chemical formula ${\text{Zn}}_x{\text{Mn}}_y{\text{Fe}}_{3-x-y}{\mathrm{O}}_4$) with core diameters of $d\sim 4$ or 15 nm produced by the fast and reproducible microwave-assisted synthesis method, and using different solvents like water or polyols. The $d\sim 4\mathrm{nm}$ MNPs were doped with ${\text{Zn}}^{2+}$, from $x=0$ to 0.9; for ${\text{Zn}}^{2+}=0.5$, ${\text{Mn}}^{2+}$ was introduced at $y=0.2,0.4$. The $d\sim 15\mathrm{nm}$ MNPs were doped with ${\text{Zn}}^{2+}$ from $x=0$ to 0.4, with ${\text{Mn}}^{2+}$ added at $y=0.1$ for ${\text{Zn}}^{2+}=0.3$ and at 0.3 for ${\text{Zn}}^{2+}=0.4$. Both sets were dispersed in water with carboxymethyl-dextran or polyacrylic acid coatings to ensure their colloidal stability, even under high magnetic fields. We highlighted the influence of the size and of the ${\text{Zn}}^{2+}/{\text{Mn}}^{2+}$ doping on the static and dynamical magnetic properties, also through the ${}^1\mathrm{H}$-NMR-dispersion profile analysis over a wide frequency range and the application of the superparamagnetic relaxation heuristic model. Larger particles exhibited higher nuclear relaxometric efficiency and anisotropy compared to the smaller ones, consistently outperforming the commercial contrast agents. On the other hand, the magnetic response and the nuclear relaxivities are enhanced by a ${\text{Zn}}^{2+}$ content of $x=0.1$ ions for approximately $4\mathrm{nm}$ MNPs and of $x=0.4$ for approximately $15\mathrm{nm}$ MNPs, while a slight enhancing effect was obtained by ${\text{Mn}}^{2+}$ introduction. It is thus shown how a proper size and doping combination provide an attractive way to modify the static and dynamical magnetic properties of MNPs by acting on different spin-spin correlation times dominating in specific frequency intervals, thus enabling the fine-tuning of image contrast properties suitable for magnetic resonance imaging.

Close

PrevNext

Reuse & PermissionsView figure in article

• 
• 
• 
• 
• 
• 
• 
• 
• 
• 
• 

• Doping effects
• Magnetic anisotropy
• Medical magnetic resonance imaging
• Spin dynamics
• Magnetic nanoparticles
• Oxides
• Magnetic resonance imaging
• Nuclear magnetic resonance relaxation rate